Produktdetails:
|
Material: | St35.8, St45.8, ST52,15Mo3, 13CrMo44, 10CrMo91 | Standard: | DIN17175, DIN2391 |
---|---|---|---|
Typ: | Nahtlos | OD: | 6mm~88.9mm |
Wandstärke: | 0.8mm~15mm | Anwendung: | KESSEL |
Oberflächentechnik: | Lack, Öl-Bad, Passivierung, phosphatierend, Strahlen | Lieferungsstatus: | Getempert, normalisiert, normalized+Tempered, usw. |
Markieren: | nahtloses Rohr des Kohlenstoffstahls,nahtlose Rohre des Kohlenstoffstahls |
Nahtloser Kohlenstoffstahl-Kessel-Schläuche DIN17175 ST45.8 Hochdruck-Rauchrohre 38,1 * 2,5 Millimeter SA213 SA210
Produktnorm: GB3087, GB5310, ASME SA210, ASME SA213, DIN17175
Hauptstahlsorten: 10,20,20G, 20MnG, 25MnG, 15CrMoG, 12Cr2MoG, 12Cr1MoVG, 12Cr2MoWVTiB, 10Cr9Mo1VNb, SA210A1-, SA210C-, SA213- T11, SA213- T12, SA213- T22, SA213- T23, SA213- T91, SA213- T92, ST45.8-/Ⅲ, 15Mo3,13CrMo44,10CrMo910 etc.
Anwendung: Für Kessel waterwall, Ekonomiser, Nachbrenner und die Dampfleitungsherstellung
Chemische Anforderungen u. mechanische Eigenschaften:
Standard | Grad | Chemische Zusammensetzung (%) | ||||||||||||||
C | Si | Mangan | P | S | Cr | MO | Cu | Ni | V | Al | W | Ti | Notiz: | N | ||
GB3087 | 10 | 0.07~0.13 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | ||||
20 | 0.17~0.23 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | |||||
GB5310 | 20G | 0.17~0.24 | 0.17~0.37 | 0.35~0.65 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | |||||
20MnG | 0.17~0.24 | 0.17~0.37 | 0.70~1.00 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
25MnG | 0.18~0.24 | 0.17~0.37 | 0.80~1.10 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
15CrMo | 0.12~0.18 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.80~1.10 | 0.40~0.55 | ≤0.20 | ≤0.30 | |||||||
12Cr2MoG | 0.08~0.15 | ≤0.50 | 0.40~0.70 | ≤0.030 | ≤0.030 | 2.00~2.50 | 0.90~1.20 | ≤0.20 | ≤0.30 | |||||||
12Cr1MoV | 0.08~0.15 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.90~1.20 | 0.25~0.35 | ≤0.20 | ≤0.30 | 0.15~0.30 | ||||||
12Cr2MoWVTiB | 0.08~0.15 | 0.45~0.75 | 0.45~0.65 | ≤0.030 | ≤0.030 | 1.60~2.10 | 0.50~0.65 | ≤0.20 | ≤0.30 | 0.28~0.42 | 0.30~0.55 | 0.08~0.15 | B 0.002~0.008 | |||
10Cr9Mo1VNb | 0.08~0.12 | 0.20~0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.00~9.50 | 0.85~1.05 | ≤0.20 | ≤0.40 | 0.18~0.25 | ≤0.015 | 0.06~0.10 | 0.03~0.07 | |||
ASME SA210 | SA210A-1 | 0.13~0.19 | ≥0.1 | 0.45~0.65 | ≤0.030 | ≤0.030 | ||||||||||
SA210C | 0.18~0.24 | ≥0.1 | 0.80~1.10 | ≤0.030 | ≤0.030 | |||||||||||
ASME SA213 | SA213 T11 | 0.05~0.15 | 0.50~1.0 | 0.30~0.60 | ≤0.030 | ≤0.030 | 1.00~1.50 | 0.50~1.00 | ||||||||
SA213 T12 | 0.05~0.15 | ≤0.50 | 0.30~0.61 | ≤0.030 | ≤0.030 | 0.80~1.25 | 0.44~0.65 | |||||||||
SA213 T22 | 0.05~0.15 | ≤0.50 | 0.30~0.60 | ≤0.030 | ≤0.010 | 1.90~2.60 | 0.87~1.13 | |||||||||
SA213 T23 | 0.04~0.10 | ≤0.50 | 0.10~0.60 | ≤0.030 | ≤0.030 | 1.90~2.60 | 0.05~0.30 | ≤0.030 | 1.45~1.75 | B0.0005~0.006 | 0.02~0.08 | ≤0.040 | ||||
SA213 T91 | 0.08~0.12 | 0.20~0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.00~9.50 | 0.85~1.05 | ≤0.40 | 0.18~0.25 | ≤0.015 | 0.06~0.10 | 0.03~0.07 | ||||
SA213 T92 | 0.07~0.13 | ≤0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.50~9.50 | 0.30~0.60 | ≤0.40 | 0.15~0.25 | ≤0.015 | 1.50~2.00 | B 0.001~0.006 | 0.04~0.09 | 0.03~0.07 | ||
LÄRM 17175 | ST45.8-/Ⅲ | ≤0.21 | 0.10~0.35 | 0.40~1.20 | ≤0.040 | ≤0.040 | ||||||||||
15Mo3 | 0.12~0.20 | 0.10~0.35 | 0.40~0.80 | ≤0.035 | ≤0.035 | 0.25~0.35 | ||||||||||
13CrMo44 | 0.10~0.18 | 0.10~0.35 | 0.40~0.70 | ≤0.035 | ≤0.035 | 0.70~1.10 | 0.45~0.65 | |||||||||
10CrMo910 | 0.08~0.15 | ≤0.50 | 0.30~0.70 | ≤0.025 | ≤0.020 | 2.00~2.50 | 0.90~1.10 | ≤0.30 | ≤0.30 | ≤0.015 |
Standard | Grad | TS (MPa) | YS (MPa) | Verlängerung (%) | Härte |
GB3087 | 10 | 335~475 | ≥195 | ≥24 | / |
20 | 410~550 | ≥245 | ≥20 | / | |
GB5310 | 20G | 410~550 | ≥245 | ≥24 | / |
20MnG | ≥415 | ≥240 | ≥22 | / | |
25MnG | ≥485 | ≥275 | ≥20 | / | |
15CrMoG | 440~640 | ≥235 | ≥21 | / | |
12Cr2MoG | 450~600 | ≥280 | ≥20 | / | |
12Cr1MoVG | 470~640 | ≥255 | ≥21 | / | |
12Cr2MoWVTiB | 540~735 | ≥345 | ≥18 | / | |
10Cr9Mo1VNb | ≥585 | ≥415 | ≥20 | / | |
ASME SA210 | SA210A-1 | ≥415 | ≥255 | ≥30 | ≤143HB |
SA210C | ≥485 | ≥275 | ≥30 | ≤179HB | |
ASME SA213 | SA213 T11 | ≥415 | ≥205 | ≥30 | ≤163HB |
SA213 T12 | ≥415 | ≥220 | ≥30 | ≤163HB | |
SA213 T22 | ≥415 | ≥205 | ≥30 | ≤163HB | |
SA213 T23 | ≥510 | ≥400 | ≥20 | ≤220HB | |
SA213 T91 | ≥585 | ≥415 | ≥20 | ≤250HB | |
SA213 T92 | ≥620 | ≥440 | ≥20 | ≤250HB | |
DIN17175 | ST45.8-/Ⅲ | 410~530 | ≥255 | ≥21 | / |
15Mo3 | 450~600 | ≥270 | ≥22 | / | |
13CrMo44 | 440~590 | ≥290 | ≥22 | / | |
10CrMo910 | 480~630 | ≥280 | ≥20 | / |
Inspektion und Test: Test der chemischen Zusammensetzung, Test der mechanischen Eigenschaften (dehnbar, Ertrag, Verlängerung), Prozesstest des eigenschaftentests (Spachtel, Erweitern, Verbiegen, Härte, Auswirkung, etc.), des Auftrittes und der Größe, Test der zerstörungsfreien Untersuchung, hydrostastic Test.
Lieferungsstatus: Getempert, normalisiert, normalized+Tempered, etc.
Oberflächenbehandlung: Ölimprägnierung, Farbe, Passivierung, Phosphatieren, Strahlen etc.
Verpacken: Export von Paket-/Holzkiste/as-Anforderung.
Kennzeichen: Wie erforderlich.
Ansprechpartner: Mrs. Yana Dong
Telefon: 13661003712, 86-10-5712 1108, 5718 5998
Faxen: 86-10-56752778